1.ANTI-RUST MECHANISM:

After coating the surface of superfine powders and pigment with some kinds of organic accessory ingredient, then processing the high-temperature treatment, it will creat a compact coat outside the surface of the pigment which will help to prevent the steel from corrasion arosed by the H₂O, oxygen and other gas after making into paint, and also strength the adhesive force of the pigments with the steel surface, which make it has an excellent antirust effect.

2.COMPONENT

Compound of a few metal salts and superfine compound powders whose surface has a high temperature coating process.

3.PERFORMANCE:

1).Compared with other antirust paints, it has an outstanding decentralization and an obvious improvement in the stability, anti-deposition and antirust property after making into paint.

2).With a good cost performance and can cut your pice cost obviously compared with other traditional antirust materials.

3).An environmental and nontoxic product with no heavy metals, it can be spray painting and brush painting, so it is an easily used, ideal and bran-new antirust product.

4.Application:

This product can replace the ZINC POWDER for making rich zinc priming paint partially and the mica iron oxide red, zinc oxide and zinc phosphate completely; so it is suitable for making all kinds of anti-rust and heavy duty anticorrosive paint.

Item

Index

appearance

Silver gray powder

Residues(on 400 mesh sieve) ,%≤

2

Specific Gravity,(g/cm³,27⁰C)

3.0~4.0

Soluble Matter in Water,g/100g

1

Oil Absorption, g/100g≤

10~25

Mater Volatile at 105⁰C,% ≤

1

PH Value of Water Slurry

7.0~9.5

Silicate(SiO₂),% ≥

18

6.Suggested dosages: 20%~40%

7.Method of Application:

General anti-rust coatings production process.

8.Packing:

25kgs or 40kgs plastic bag inner and plastic woven bag outer.

9. Storage:

Keep it in a dry and ventilated place.